Material and Application Guide
|
| |
|
Phone: (313)
429-LEVY |
|
Fax: (313)
429-2448 |
|
E-Mail: sales@edwclevy.net |
| |
| Material: |
|
Expanded
Blast Furnace Slag |
| |
|
|
| Product: |
|
LWB
(BF) –
ASTM |
| |
|
|
| Application: |
|
Blended
aggregate for medium weight masonry block
|
| |
|
|
| Description: |
|
A blend of coarse and fine aggregate, produced by crushing and screening expanded iron Blast
Furnace Slag. A light brown to gray crystalline aggregate formed simultaneously with the production of iron in a blast
furnace. The particles are sized from 3/8” (9.5mm)to zero (dust). |
 |
 |
|
LWB
Expanded Blast Furnace Slag
|
|
| Specifications: ASTM |
| |
| LWB
expanded Blast Furnace Slag conforms to all the requirements of The American Society for
Testing and Materials (ASTM) C 331, combined fine and coarse aggregate, 3/8 in. (9.5-mm) to 0 |
|
|
| U.S. Sieve |
1/2" |
3/8" |
#4 |
#8 |
#16 |
#50 |
#100 |
#200 |
| Metric Sieve |
12.5mm |
9.5mm |
4.75mm |
2.36mm |
1.18mm |
300µm |
150µm |
75µm |
| Specification |
100 |
90-100 |
65-90 |
35-65
|
-
|
10-25
|
5-15
|
-
|
| General
Usage Guide: |
| |
| The
LWB expanded Blast Furnace Slag should be blended into the masonry mixture along with the
cement, water and any other special additives or admixtures in the proportions detailed in
the mix design. Depending on the specific mix
design, other coarse and/or fine aggregates may also be needed to be blended into the
masonry mixture. |
| Levylite
Slag Block Mix Design:
U.S.
(lbs per 1 cy. yd.)
| Type 3 portland Cement |
650 lbs |
| LWB Expanded Blast Furnace Slag |
3250 lbs |
Metric
(kgs per 1 m3)
| Type 3 portland Cement |
385 lbs |
| LWB Expanded Blast Furnace Slag |
1930 lbs |
|
| Supply
Location: |
| |
|
· Levy Plant #1
|
| This information
is not to be taken as warranty or representation for which we assume legal responsibility
nor as permission or recommendation to practice any patented invention without a license.
It is offered solely for your consideration, investigation and verification. |
| |